hot pressed sintering meaning in Chinese
热压烧结
Examples
- This thesis reports some results on the hot press sintering of nano - composite wc - co powder , which is prepared by spray pyrogenation & continuous deoxidization and carbonization process
本课题采用热压烧结技术对以喷雾热解?连续还原碳化法制备的纳米复合wc - co粉末进行了热压烧结研究。 - The sintering time also affects the specimens " properties . nano - composite wc - co powder can be hot press sintered to cermet whose hra is 94 . 6 and trs is 1183 mpa under 1350 for 2 hours
最终烧结实验表明纳米复合wc - co粉末1350保温2小时条件下的热压烧结可以获得抗弯强度为1183mpa ,洛氏硬度为94 . 6的硬质合金。 - The experimental techniques ( such as sedimentation equipment , controlling the size and size distribution of powders , the concentration of suspension ) have been devised subtly . on the basis of theoretical and densification design , the w - mo - ti fgm has been obtained by particle settling and hot pressing sintering . the structures of specimen were observed by electron probe
通过对实验工艺,如沉降设备、原料粒度及粒度分布的控制、悬浮液浓度等方面进行精细的设计,在理论设计和致密化研究的基础上,通过颗粒共沉降得到梯度沉积体,并通过真空热压烧结得到w - mo - ti功能梯度材料。